Coverage Kit

Woven high-density polyethylene (HDPE) black fibres fabric laminated on both sides with white low density polyethylene (LDPE) coating

Woven black HDPE fibres fabric and coated with grey LDPE on the outside

Minimum 100N under ISO 4674-1B 2003, with a test piece of 200 x 200mm as described in ISO 4674 annex B, in plain sheet

Minimum 500N and 15% to 35% elongation in warp and weft in plain sheet under ISO 1421-1

The tarpaulin tensile strength under ISO 1421-1 after 1500 hours UV under ASTM G53/94 (UVB 313 nm peak) must be: Minimum 80% of the original value of the actual product, and not less than 475N. To be tested in the plain sheet

Minimum 700N inside the reinforcement bands as per ISO 1421-1, pulling lengthwise in a pre-punched hole of 8mm with a hook of 8mm wire diameter. To test in 2 holes in each side bands

The reinforcement bands tensile strength under ISO 1421-1 after 1500 hours UV under ASTM G53/94 (UVB 313 nm peak) must be: Minimum 80% of the original value of the actual product, and not less than 665N

Only one welding allowed, in the middle of the sheet, length wise. The tarpaulin tensile strength crossways at the place of the welding under ISO 1421-1 must be: Minimum 50% of the original value of the actual product, and not less than 400N

Flame retardant EN13823+A1 Minimum class D, s2, d2

White sun reflective on both sides of the sheet without fluctuation in color. Grey coating on the outside of the bands

2 years minimum